摘要：本论文主要是测试了不同填料对聚氨酯橡胶机械性能的影响、不同填料用量对聚氨酯橡胶机械性能的影响、不同加料顺序对聚氨酯橡胶机械性能的影响、偶联剂对聚氨酯橡胶机械性能的影响这四个方面。由实验得出气相白炭黑、沉淀法白炭黑和炭黑对聚氨酯橡胶都有较好的补强效果，而硅藻土对于聚氨酯橡胶的补强效果稍差，是半补强填料。在不同炭黑用量对于聚氨酯橡胶性能的比较中，可以得出加入30份炭黑制得的聚氨酯橡胶的机械性能性对较佳。炼胶过程中，将DCP先于填料加入相较填料先于DCP加入，不但加工性能有所提高，机械性能也有显著的提高。加入偶联剂后，聚氨酯橡胶的机械性能有了明显的提高。5350
- 上一篇：水性丙烯酸树脂的交联技术研究+文献综述
- 下一篇：甲醇铁钼催化法制甲醛的工艺设计
关键词： 聚氨酯橡胶；填料；炭黑；硅藻土
Effect of Fillers on Mechanical Properties of Polyurethane Rubber
Abstract: The experiments test the effects of different fillers on the mechanical properties of PUR, the effects of different content of fillers on the mechanical properties of PUR, the effects of different feeding sequence on mechanical properties of PUR, the effects of coupling agent on the mechanical properties of PUR influence. Experimental results indicate that: fumed silica、Precipitated silica and carbon black has good reinforcing effect of polyurethane rubber. And diatomite hasn’t good reinforcing effect of polyurethane rubber, so it is the semi reinforcing filler. From effect of different amount of carbon black of polyurethane rubber, we know that the mechanical properties of PUR with 30 parts of carbon black are good. In the process of mixing polyurethane rubber, adding DCP into PUR before adding fillers can improve the processing performance and mechanical properties. After adding the coupling agent, the mechanical properties of polyurethane rubber has been significantly improved.
Key Words: polyurethane rubber (PUR)；fillers；carbon black；diatomite
目录
摘要 i
Abstract i
目录 ii
1 绪论 1
1.1 聚氨酯橡胶 1
1.1.1 聚氨酯橡胶的分类 1
1.1.2 聚氨酯橡胶的性能 1
1.1.3 聚氨酯的历史和前景 1
1.2 填料 2
1.2.1 填料的种类与介绍 3
1.2.2 填料的选择 7
1.2.3 填料的主要性能 8
1.3 填料对聚氨酯橡胶的影响 8
1.3.1 炭黑对聚氨酯橡胶的影响 8
1.3.2 陶土对聚氨酯橡胶的影响 9
1.3.3 填料的表面改性 10
1.4 课题的目的 11
1.5 研究内容和目标 12
1.5.1 研究内容 12
1.5.2 研究目标 12
2 实验部分 13
2.1 实验原材料和药品 13
2.2 实验用仪器设备 13
2.3 试样制备 14
2.3.1 配方 14
2.3.2 制备过程 14
2.4 测试与表征 15
2.4.1 硫化特性的测定 15
2.4.2 硬度测试 15
2.4.3 拉伸性能测试 16
2.4.4 撕裂性能测试 16