摘要金属材料使用过程中的失效大多开始发生在表面，比如疲劳断裂，接触疲劳，磨损和腐蚀等等。这些失效对结构和材料表面的性能十分敏感。因此，改善材料表面组织结构来提高表面的性能能很好的延迟表面失效的发生，从而延缓材料的使用寿命。64036

本文通过对纯铜表面进行机械研磨处理，从而达到细化表面晶粒的效果。由于加工设备处于起步试验阶段，因此本文设想通过改变试验参数，研究在不同条件下处理达到的效果，获得一条合适的工艺线路。采用金相显微镜、显微硬度计对处理后试样的微观组织结构和性能进行了表征。

毕业论文关键词表面机械研磨处理，组织，变形层，粗糙度，显微硬度

毕业设计说明书（论文）外文摘要

Title Study of the Surface Nano-processing on the Pure Copper

Abstract The metal materials start to loss efficacy in the surface when they are used, such as fatigue fracture, contact fatigue, wear, corrosion and so on. The structure and surface of materials have a major impact on the lossing efficacy. So, improving the surface properities by changing the structure of the surface can postpone the lossing efficacy, in order to delay the service life of materials.

In this paper, through to mechanical grind the surface of pure copper, thining the surface grain. Because the development of the equipment was just starting, the main purpose of the experiment is researching the different results in the different experiment conditions by changing the experiment parameters.So that,we can obtain a suitable process route. And we charactered the microstructure and properity of the samples that had been treated by the metallurgical microscopy and microhardness tester.

Keywords mechanical polishing surface treatment, weave, deformation layer, roughness, microhardness

1 绪论 1

1.1 研究的意义及目的 1

1.2 研究现状 1

2 实验材料和方法 5

2.1 实验设备简介 5

2.2 实验流程 5

2.3 实验材料及制备过程 6

2.4 试样结构和性能表征 7

3 实验结果与讨论 7

3.1 纯铜表面喷丸处理后的表观特征结构特征 7

3.2 纯铜表面喷丸处理后的性能 12

4 预期与改善 14

结论 16

致谢 17

参考文献 18

1 绪论

1.1 研究的意义及目的

在工业上，工程金属材料用途广、用量大，利用纳米技术来提高工程金属材料的综合性能有着巨大的应用前景。材料的组织结构影响甚至决定着材料的使用性能，人们提出多种表面改进的技术来满足材料在不同环境下的使用要求，如电镀、喷丸、气相沉积(PVD、CVD)、激光处理、喷涂和表面化学处理等，这些技术是材料的表面性能得到很大的改善，从而很好地提高了材料的服役行为，因此得到广泛的使用。

纳米材料具有独特的结构和优异的性能[1]，如高的硬度和强度，强化的物理性能[2,3],优异的摩擦性能[4],低温超塑性[5,6]等等。纳米材料制造的器件，也就具有非常优异的使用性能。对于工程材料而言，现有的纳米制造工艺并不能满足其制造要求，人们提出了诸多在工程材料表面实现纳米化，从而来改善其使用性能。本毕业设计利用表面研磨技术就纯铜如何实现表面纳米化开展研究。