摘要本论文通过向钨系延期药中添加纳米CuO ，筛网干混，配制不同配方的改性延期药，考察纳米材料对钨系延期药热分解性能以及燃烧性能的影响。
- 上一篇：固体云爆剂制备方法及性能表征
- 下一篇：稀土离子PLLA复合纳米纤维膜的制备与性能研究
采用多种方法制备纳米材料并利用 XRD 对纳米材料进行表征，采用TG和 DTA 方法考察钨系延期药的热分解特性，结果表明，加入纳米CuO后，钨系延期药放热峰起始值变化随纳米材料CuO的变化而变化。吸热峰和放热峰起始温度变化不大，纳米材料的添加，催化作用较为明显。8662
通过测量按不同配比添加纳米CuO的钨系延期药的燃速，实验研究了纳米材料对钨系延期药燃烧性能的影响。结果表明，纳米CuO对钨系延期药的燃速有催化作用，量不同有不同的催化效果，添加配比为1%、6%、8%，提高钨系延期药的燃速，纳米CuO添加配比为2%、4%降低钨系延期药的燃速。但是纳米材料的粒径才是影响燃速的主要因素。
关键词 纳米材料 钨系延期药 热分析 燃速
毕业设计说明书（论文）外文摘要
Title Experimental Study on Combustion Performance of Long Seconds Delay Composition was Modified from Nanomaterial
Abstract
Tungsten type delay composition was prepared by dry-mixing method,through the addition of nano-CuO ,thermal decomposition and combustion capability of tungsten type delay composition were studied.
The nature of nanomaterials was tested by XRD and Electron Microscope, thermal decomposition characteristics of tungsten type delay composition were studied by TG and DTA methods.The results show that Tungsten type delay exothermic peak starting value change with the changes of nanomaterials CuO change after adding nano-Cuo.Endothermic peak and exothermic peak onset temperature change is small, the addition of nano-materials makes the catalytic effect is more obvious.
By measuring the burning rate of the tungsten type delay to add different proportions of CuO, the experimental study of the impact of nanomaterials on the combustion performance of the tungsten type delay. The results show that Nano-CuO catalyst of tungsten type delay burning speed, different amount of different catalytic effect. Improve tungsten type delay the burning rate by adding the ratio of 1%, 6%, 8%, reduce tungsten type delay of the burning rate by adding the ratio of 2%, 4%. However, the particle size and crystal shape of the nanomaterials is the impact of the burning rate of the main factors.
Keywords nano-materials tungten type delay composition
thermal analysis burning rate
目录 Ⅰ
1 绪论 1
1.1 研究背景及意义 1
1.2 纳米材料概况 1
1.3 纳米材料在火工药剂方面应用 2
1.4 延期药概况^ 3
1.5 影响延期药燃速的因素 4
1.6 要研究问题和拟采用的研究手段 4
2 纳米材料的制备及表征 5
2.1 纳米材料的制备 5
2.2 纳米材料的表征 7
3 钨系延期药的制备 9
3.1 钨系延期药配方的选择 9
3.2 钨系延期药的制备实验 10
3.3 小结 11
4 钨系延期药的热分解性能分析 11
4.1 热分析方法 12
4.2 钨系延期药样品的差热分析 12
5 钨系延期药的燃烧特性研究 16
5.1 燃烧传播机理 16
5.2 钨系延期药燃速测试 17
结论 19
致谢 20
参考文献 21
1 绪论
-
金属改性芦苇活性炭对重金属的吸附性能研究
-
活性炭的改性及其对磷吸附的实验研究
-
球状石墨微纳米材料的制备与性能研究
-
改性的介孔材料SBA-15合成和表征
-
改性介孔硅基材料SBA-15（...
-
化学改性碳黑作为阴极材...
-
改性硝酸盐型烟火药安全氧化剂生产工艺研究
电站锅炉暖风器设计任务书
乳业同业并购式全产业链...
大众媒体对公共政策制定的影响
杂拟谷盗体内共生菌沃尔...
中考体育项目与体育教学合理结合的研究
当代大学生慈善意识研究+文献综述
java+mysql车辆管理系统的设计+源代码
十二层带中心支撑钢结构...
河岸冲刷和泥沙淤积的监测国内外研究现状
酸性水汽提装置总汽提塔设计+CAD图纸