摘要：本实验选择了乙烯裂解装置副产脱除异丁烯后的剩余碳四作为原料。分别在1050℃和900℃温度下焙烧4小时制得两种载体A,B，并用含Pd的金属盐溶液进行浸渍。把两种催化剂在实验评价装置上进行评价得出焙烧温度为1050℃的载体A对1-丁烯的选择性较好。继而开始用载体A测定活性组分含量对催化剂性能影响，实验数据表明浸渍0.28（m/m）%的Pd所得到的催化剂是醚化后裂解碳四选择性加氢脱丁二烯制高纯度1-丁烯合适的催化剂。24423
- 上一篇：卟啉复合薄膜的组装+文献综述
- 下一篇：酸性离子液体降解木质素制备芳香醛
用上述催化剂进行工艺操作条件的研究，针对不同温度，压力，空速，氢比分别进行了几组实验。工艺操作条件研究结果表明，该催化剂的合适工艺操作条件为：压力1.5MPaG~2.0MPaG，温度为50℃~80℃，空速为10h-1，氢比为3mol/mol。
最后为了检验催化剂各种性能的稳定性进行了500小时的稳定性实验。得出结论丁二烯的转化率、1-丁烯的收率均达到指标要求，说明该催化剂的加氢活性及选择性均具有良好的稳定性。
毕业论文关键词： 碳四；载体；Pd金属盐溶液；工艺操作条件；稳定性实验
Mixed C4 selective hydrogenation of butadiene removal system 1-butylene catalysts
Abstract : This study selected the ethylene cracker unit byproduct removal of residual carbon after four isobutylene as a raw material .After calcining 4 hours , respectively to obtain two vectors A, B at a temperature of 1050 ℃ 900 ℃, and impregnated with a solution containing Pd metal . The two catalysts in the experimental evaluation of the evaluation means to selectively draw the firing temperature of the carrier A 1050 ℃ preferably 1-butylene . Then start the measurement of the active ingredient content on catalyst performance carrier A, experimental data show that the catalyst impregnated 0.28 (m / m)% of Pd is obtained after ether cleavage selective hydrogenation of carbon four high purity de- butadiene system 1-butylene suitable catalysts.
Research conducted by the above process conditions the catalyst for the different temperature, pressure, space velocity and hydrogen ratio were carried out several experiments . Process operating conditions results show that the catalyst suitable process operating conditions are as follows: pressure 1.5MPaG ~ 2.0MPaG, the temperature is 50 ℃ ~ 80 ℃, space velocity 10h-1, hydrogen ratio 3mol/mol.
Finally, to test the stability of various properties of the catalyst stability experiments conducted for 500h . Concluded that the conversion of the butadiene , 1-butylene closing rate reaches the indicator , indicating the hydrogenation activity and selectivity of the catalysts have good stability.
Keywords: Carbon four; carrier; Pd salt solution; process operating conditions; stability test
目 录
1 绪论 1
1.1 化学反应与催化剂 1
1.1.1 热力学与动力学 1
1.1.2 催化剂活性、选择性、稳定性 1
1.1.3 化学反应 1
1.2 1-丁烯的概况 2
1.2.1 1-丁烯的基本性质 2
1.2.2 1-丁烯产品生产工艺 2
1.2.3 1-丁烯的应用 3
1.3 研究意义及目的 3
1.3.1 研究意义 3
1.3.2 研究目的 3
1.4 国内外的发展概况及存在的问题 4
1.5 研究方法及内容 4
1.5.1 研究方法 4
1.5.2 研究内容 5
2 实验部分 6
2.1 催化剂制备部分 6
2.1.1 催化剂制备所需原料 6
2.1.2 催化剂制备所需设备 6
2.1.3催化剂的制备流程 7
-
纳米Trögersbase衍生物催化...
-
X70碳钢表面硅烷膜缓蚀作用的研究
-
简单有效的方法合成2-苄基...
-
基于醚四酸MOFs的构筑及其对pH的传感
-
碳纤维负载CoPB制氢催化剂的制备
-
5-氨基四唑/碱式硝酸铜气...
-
化学改性碳黑作为阴极材...
酸性水汽提装置总汽提塔设计+CAD图纸
河岸冲刷和泥沙淤积的监测国内外研究现状
电站锅炉暖风器设计任务书
十二层带中心支撑钢结构...
java+mysql车辆管理系统的设计+源代码
杂拟谷盗体内共生菌沃尔...
当代大学生慈善意识研究+文献综述
大众媒体对公共政策制定的影响
乳业同业并购式全产业链...
中考体育项目与体育教学合理结合的研究