摘要:本文通过甘氨酸燃烧法制备锆酸镧陶瓷粉，研究了反应时间、反应温度、甘氨酸用量对锆酸镧陶瓷粉性能的影响，以及探讨了钕部分取代镧对产物性能的影响，实验最后通过XRD、EDS和SEM对产品进行表征。从X衍射图分析可知，当温度为750度时，产物特征衍射峰强度高，峰型尖锐，衍射峰半高宽较窄，说明产物的晶体结构比较完整，结晶性比较好；随着反应时间的延长，锆酸镧陶瓷粉的晶体平均粒径增大，结晶度增加，特征衍射峰强度增强，衍射峰的半高宽变窄，可知晶型越来越好；当Gly/M即甘氨酸摩尔量比上金属离子的摩尔总量（La3+和Zr4+）为2:1时，锆酸镧的特征衍射峰十分明显，从出峰情况可以看出此时产物的晶体结构完整，已合成出锆酸镧纳米晶；钕掺杂制备分子式为(LaxNdy)2Zr2O7的产物，当y为0、0.3、0.4时，随着钕元素含量的增加，晶体的平均粒径在减小，产物的聚合度在下降。从EDS图像分析可知，锆酸钐的原子比（Zr、Sm、O）接近2:2:7，而锆酸镧的原子比（La、Zr、O）则为2:3.4:8.4，与理论结果相差较大，可能是由于仪器误差造成的。从SEM图像分析可知，锆酸钐的致密性低，比较松散；而锆酸镧晶体表面有很多细孔，且团聚现象比较明显。20912
- 上一篇：HJ663-2013对广州城市空气质量进行研究
- 下一篇：乙烯装置丙烯精馏塔设计+CAD图纸
毕业论文关键词：热障涂层；陶瓷；涂层性能；锆酸盐
Neodymium and samarium's effect on the properties of lanthanum zirconate ceramics powder
Abstract :In this paper, the method of glycine combustion is used to prepare lanthanum zirconate ceramics, It is studied on the different effects on anthanum zirconate ceramics powder caused by the difference of reaction time, reaction temperature and dosage of glycine ,Apart from this ,this paper also discusses the effect on the product properties caused by neodymium replace part of the lanthanum. In the last ,the products are characterized by XRD, EDS and SEM. The research results show that when the temperature is 750 degrees, the product shows all the characteristics of diffraction peak, and the diffraction peak intensity is high and sharp, the crystalline structure of the product is complete; As the extension of reaction time, crystal average particle size of lanthanum zirconate ceramics powder increases, the crystallinity increases, the characteristics of the diffraction peak intensity is enhanced, and a half high width of the diffraction peak Narrows, so the crystal structure is more perfect; When Gly/M is 2:1, the characteristic diffraction peak of lanthanum zirconate is very clear, crystal structure is complete, thus zirconate nanocrystals of lanthanum have been made; Neodymium is doped with the preparation of the product of the formula for the (LaxNdy)2 Zr2O7, when y is 0, 0.3, 0.4, with the increase of content of neodymium, average particle size in the crystal decreases, and the degree of polymerization of product is falling. For the SEM image analysis, atomic ratio of zirconate samarium (Zr, Sm, O) is close to 2:2:7, and atomic ratio of lanthanum zirconate (La, Zr, O) is 2:3.4:8.4, is a little far different of the theoretical results, may be it is caused by the instrument error. EDS image analysis shows that the density of zirconate samarium is low, relatively loose; And the crystal surface of lanthanum zirconate has many pores, and reunion phenomenon is more obvious.
Keywords: thermal barrier coatings ; ceramic ; coatiang performance；zirconate
目录
1前言 1
1.1热障涂层陶瓷材料 1
1.1.1传统热障涂层陶瓷材料 1
1.1.2新型热障涂层材料 1
1.2稀土元素 3
1.3溶盐法 3
1.4固相反应法 4
1.5溶胶-凝胶技术 5
1.6共沉淀法 6
1.7低温燃烧合成法 6
-
基于非对称六羧基配体的...
-
含脲基的金属-有机框架材...
-
高频导磁体对填充式电化学反应器性能的影响
-
NHC-Pd化合物在催化溴代苯...
-
金属改性芦苇活性炭对重金属的吸附性能研究
-
微生物菌剂对污泥好氧发...
-
基于醚四酸MOFs的构筑及其对pH的传感
中考体育项目与体育教学合理结合的研究
大众媒体对公共政策制定的影响
河岸冲刷和泥沙淤积的监测国内外研究现状
当代大学生慈善意识研究+文献综述
十二层带中心支撑钢结构...
酸性水汽提装置总汽提塔设计+CAD图纸
杂拟谷盗体内共生菌沃尔...
java+mysql车辆管理系统的设计+源代码
乳业同业并购式全产业链...
电站锅炉暖风器设计任务书