摘要：本文研究了改性剂和各种硬化工艺对水玻璃砂溃散性能的影响。采用的改性剂有：聚丙烯酰胺、十二烷基磺酸钠。采用的单一硬化工艺有：烘干硬化、吹CO2气体硬化。采用的复合硬化工艺有：有机酯-吹CO2气体硬化。实验结果表明：水玻璃加入量越低，残留强度越小，水玻璃砂溃散性越好。在水玻璃加入量一定时，加入了改性剂的水玻璃砂残留强度低于未加入改性剂的，其溃散性更好。吹二氧化碳加有机酯硬化和烘干硬化、吹二氧化碳硬化相比，残留强度低，溃散性越好。吹气加有机酯硬化时，改性剂为聚丙烯酰胺，加入量0.3~0.9%，吹气时间越长残留强度越低，溃散性越好；改性剂为十二烷基磺酸钠，加入量0.3~0.9%吹气时间越短残留强度越低，溃散性越好。20718
- 上一篇：护手霜的流变性研究+文献综述
- 下一篇：电解铜箔表面电镀铜改性工艺研究
毕业论文关键词：有机酯；改性剂；CO2吹气硬化；水玻璃砂；溃散强度
Research on Effect of Modification agent of Water Glass Sand Collapsibility Strength
Abstract: The effect of modification agent and hardening process on properties of water glass sand was studied. The modified agents of Polyacrylamide and sodium dodecylsulphate were used. Single hardening processes which were used were dried hardening, blowing CO2 gas hardening. Compound hardening processes which was used was organic ester - blowing CO2 gas hardening. The experimental results showed that: the addition of water glass content is low, the residual strength is small ,collapsibility is better. Water glass add a certain amount of time, adding the modifier of water glass sand residual strength is lower than that of the non modified agent good collapsibility. Blowing CO2 and organic ester hardening and drying and hardening, blowing CO2 hardening, hardening effect is better good collapsibility. Blowing hardening, modifier polyacrylamide, adding 0.3~0.9 percent, blowing time more long residual strength the lower the better collapsibility; modifier is sodium dodecylsulphate, adding 0.3~0.9 percent, blowing time shorter residual strength is low collapsibility is better.
Key words: Organic ester; Modification agent; CO2 gas hardening; Water glass sand; Collapsibility Strength
目录
1.前言 1
1.1水玻璃简介 1
1.2水玻璃的发展 2
1.3水玻璃的改性 2
1.3.1.水玻璃的物理改性 3
1.3.2.水玻璃的化学改性 3
1.3.3.水玻璃的复合改性 4
1.4水玻璃砂溃散性能研究进展 5
1.4.1溃散剂 5
1.4.2水玻璃改性 6
1.4.3硬化工艺 6
1.5选题的目的和意义 7
1.6课题的研究内容和目标 8
1.6.1研究内容 8
1.6.2研究目标 8
2.实验 9
2.1试验材料 9
2.2 试验方案 9
2.2.1未改性水玻璃加入量对水玻璃砂溃散性能的影响 9
2.2.2改性剂加入量对水玻璃砂溃散强度的影响 9
2.2.3硬化工艺对水玻璃砂溃散强度的影响 10
2.2.4吹气时间对水玻璃砂溃散强度的影响 10
2.2.5改性剂加入量和吹气时间对水玻璃砂溃散强度的影响 11
2.2.6改性水玻璃加入量和吹气时间对水玻璃砂溃散强度的影响 11
2.3试验设备 12
2.3.1 SHN辗轮式混砂机 12
2.3.2 XQY-Ⅱ智能型砂强度机 13
2.3.3 SAH树脂砂制样机 13
2.3.4 SX-4-10箱式电阻炉 14
2.3.5 101-3型干燥箱 14
2.3.6 JB50-D搅拌器 15
-
基于非对称六羧基配体的...
-
含脲基的金属-有机框架材...
-
高频导磁体对填充式电化学反应器性能的影响
-
NHC-Pd化合物在催化溴代苯...
-
金属改性芦苇活性炭对重金属的吸附性能研究
-
微生物菌剂对污泥好氧发...
-
基于醚四酸MOFs的构筑及其对pH的传感
乳业同业并购式全产业链...
电站锅炉暖风器设计任务书
大众媒体对公共政策制定的影响
河岸冲刷和泥沙淤积的监测国内外研究现状
杂拟谷盗体内共生菌沃尔...
十二层带中心支撑钢结构...
当代大学生慈善意识研究+文献综述
中考体育项目与体育教学合理结合的研究
酸性水汽提装置总汽提塔设计+CAD图纸
java+mysql车辆管理系统的设计+源代码