摘要：本文主要用购自北京的JAM-II膜作为主要的阴离子交换膜进行，并同时用所购买的上海阴离子交换膜和山东阴离子交换膜进行对比实验。通过实验最终确定使用JAM-II膜。同时使用扫描电镜（SEM）对阴离子交换膜进行必要的表征。结果表明所用于试验的阴离子交换膜由于种类、制作工艺的不同，其在扫描电镜下所呈现的表征图也不同。
- 上一篇：B、Mg、Al对DBAP燃烧剂燃烧性能影响研究
- 下一篇：MOF/石墨烯复合材料的组装及在超级电容器中的应用
本次课题中，主要用所购买的离子液体（1-辛基-3-甲基咪唑双三氟甲磺酰亚胺盐）作为主要的油相支持电解质，0.5M的氯化钾溶液作为水相支持电解质，构筑阴离子交换膜支撑的两互不相溶界面。
利用循环伏安法（CV）来研究在该界面上尺寸选择性离子转移反应。结果表明，使用阴离子交换膜所构筑的两互不相溶液液界面可以到到一个较宽的电化学窗口。（-0.5v-1.0v）并利用ClO4-、SO42-、NO2-阴离子来研究在该界面上的尺寸选择性离子转移反应。结果表明，该阴离子在此电化学窗口下发生了离子转移反应，既从水相转移到油相之中。20564
毕业论文关键字 ：阴离子交换膜；离子液体；两互不相溶界面；循环伏安；离子转移
Studies on the Electric charge Transfer Behaviors across the two Immiscible Interface Supported by Anion-Exchange Membrane
Abstract: in this paper, JAM-II membrane from Beijing was used as a main anion-exchange membrane, meanwhile, anion-exchange membranes from Shanghai and Shandong were also applied in this experiment. Through the research，JAM-II membrane was proved to the best one. The scanning electron microscopy (SEM) was used to characterize those above membrane materials, and the results show that different anion-exchange membranes had their own characteristics in SEM because of their different kinds and production process.
In the work, the commercially available room temperature ionic liquids ( 1-octyl-3- methylimidazolium bis(trifluoromethylsulfonyl)imide ) were used as main supporting electrolyte of oil phase, while potassium chloride solution which the concentration is 0.5M was used as supporting electrolyte of water phase, and then both of the phases were used to build two immiscible interface supported by anion-exchange membrane.
Using cyclic voltammetry (CV) method to study on size-selective ion transfer behaviors at this interface. And results show when using that two immiscible interface supported by anion-exchange membrane, I can get a better electrochemical window. (-0.5v-1.0v) ClO4-、SO42- 、NO2-anions were used to research the size-selective ion transfer behaviors at this interface. It shows that ion transfer reaction had taken place at this electrochemical window, which means ions had transfer from water phase to oil phase.
Keywords: anion-exchange membrane ；room temperature ionic liquids ；two immiscible interface ；cyclic voltammetry ；ion transfer
目录
1 绪论 1
1.1 选题研究目的和意义 1
1.2 选题研究现状及发展趋势 2
1.2.1 离子交换膜 2
1.2.2 双电层及Ｄｏｎｎａｎ理论 3
1.2.3 离子液体 4
1.2.4 离子液体/水界面电化学 5
2 实验部分 6
2.1 仪器与试剂 6
2.1.1 试剂 6
2.1.2 仪器 7
2.1.3 试剂与药品配制 8
2.2 实验内容 8
2.2.1 实验原理 8
2.2.2 阴离子交换膜的表征 9
2.2.3 构筑阴离子交换膜支撑的两互不相溶界面 9
2.2.4 研究在该界面上的尺寸选择性离子转移反应 10
2.2.5 实验流程图、示意图和装置图。 11
-
X70碳钢表面硅烷膜缓蚀作用的研究
-
基于Al/Ni纳米复合薄膜热源...
-
化学改性碳黑作为阴极材...
-
Cu掺杂对Mn-Co尖晶石型化合...
-
聚乙烯醇凹凸棒粘土渗透汽化膜的制备与表征
-
TiO2-纳米凹凸棒石光催化膜制备研究
-
陶瓷膜微滤澄清纤维素酶发酵液实验研究
十二层带中心支撑钢结构...
大众媒体对公共政策制定的影响
河岸冲刷和泥沙淤积的监测国内外研究现状
当代大学生慈善意识研究+文献综述
乳业同业并购式全产业链...
电站锅炉暖风器设计任务书
酸性水汽提装置总汽提塔设计+CAD图纸
杂拟谷盗体内共生菌沃尔...
中考体育项目与体育教学合理结合的研究
java+mysql车辆管理系统的设计+源代码