摘要：针对国内防污涂料技术落后的现状，本文开展环氧改性有机硅涂料的应用研究，为开发无毒减阻的环氧改性有机硅低表面能防污涂料提供科学的基础。本文针对构成涂料的成膜物质，系统地研究了有机硅涂料的制备、表面特性以及涂料的固含量。研究表明，固化剂为树脂质量的4%、颜基比为4.5:5、滑石粉为颜填料的2%、分散剂为涂料总量的4%、流平剂为涂料总量的3%时，涂料性能较好。关键字：环氧改性有机硅树脂；低表面能涂料；防污；接触角6874
- 上一篇：Al-Si-Ca脱氧剂脱氧能力研究+实验分析
- 下一篇：新型聚氨酯阻燃材料研究+文献综述
Research of low surface energy coatings
Abstract：Antifouling paint technology for the domestic backward status, the paper carried silicone coating applied research, for the development of non-toxic silicone drag reduction low surface energy antifouling coatings to provide a scientific basis. This film-forming material for the coating composition of preparation, silicone coatings, surface properties, and coating solids are systematic studied. The studies show that the coating performance is better when the curing agent content of 4%, pigment to binder ratio of 4.5：5, talc 2% of the pigment, dispersing agent is 4% of a solvent, a leveling agent is 3% of the solvent.
Key words：Silicone；low surface energy coatings；antifouling；contact angle
目 录
1 绪论 1
1.1 低表面能涂料的发展趋势 1
1.2 低表面能涂料的性能 1
1.3 低表面能涂料的用途 2
1.4 低表面能涂料技术发展现状 2
1.5 本课题的研究意义 3
2 实验部分 3
2.1 实验原料来源及其规格 3
2.1.1 低表面能树脂制备原料 3
2.1.2 低表面能涂料制备原料 4
2.2 实验机理、反应 4
2.2.1 有机硅树脂改性机理 4
2.2.2 低表面能防污涂料防污机理 6
2.3 制备工艺 6
2.3.1 环氧改性有机硅树脂的制备 6
2.3.2 低表面能涂料的制备 7
2.4 涂料的性能测试 8
2.4.1 干燥时间 8
2.4.2 流平性 8
2.4.3 耐盐水、耐水性（浸泡法） 8
2.4.4 光泽度 8
2.4.5 细度 9
2.4.6 涂料的固含量 9
2.4.7 接触角 10
3 结果与讨论 11
3.1不同溶剂对涂层性能的影响 11
3.2固化剂含量对涂层性能的影响 11
3.3颜基比的不同对涂层性能的影响 13
3.4分散剂含量对涂层性能的影响 14
3.5流平剂含量对涂层性能的影响 14
4 研究结论 16
致谢 17
参考文献 18
附录一 涂料制备实验装置 19
附录二 性能测试仪器 19
附录三 不同涂料配方对照组 21
1 绪论
1.1 低表面能涂料的发展趋势
据资料记载，在世界各地的海域中有2000多种附着生物。这些附着生物的幼虫和孢子在海洋中漂浮游动当它们发育到一定程度就在船底附着、定居并进一步繁殖。这些生物附着会增加船底表面粗糙度、使船舶的航速下降、燃油消耗量增加（最高可达到30%），也会增加海水管道输送阻力；这些生物生长会产生一种张力，这种张力能剪开和破坏船底漆膜。同时这些生物还会分泌出有机酸，使船底钢板及水下设施的腐蚀破坏加剧、使用寿命显著缩短。为解决此问题各种船舶防污涂料便应运而生。传统的防污涂料是通过防污剂的渗出对附着生物进行毒杀达到防污目的。这种方法或多或少会污染环境，因此人们正尝试从新的思路来设计研制防污涂料：一方面寻找防污高分子材料对一些生物的表皮状态进行模仿；另一方面寻找合适的天然防污剂，在不破坏环境的前提下防止生物附着。[3,4]