摘要本论文通过对NC的结构特点分析，在NC中添加扩链剂和增强剂来研究对其力学性能的影响。选用了聚醚多元醇作为扩链剂，异氰酸酯IPDI作为增强剂，研究不同配料配比下对NC力学性能的影响。研究表明：聚醚多元醇的加入对体系的力学性能的增强效果明显。在其他条件不变的情况下改变IPdI的量为1%的时候NC的力学性能较好，当IPDI不变时，聚醚多元醇含量为2%时力学性能较好。6132
- 上一篇：两层挠性覆铜板用聚酰亚胺材料的制备
- 下一篇：聚酰亚胺二层挠性覆铜板的制备与应用
关键词 NC IPDI 聚醚多元醇 力学性能
毕业设计说明书（论文）外文摘要
Title Study on the Enhancement of mechanical properties of polyether polyurethane system
Abstract
In view of the network structure of NC，through increasing the chain extension in NC ,the influence of the mechanical properties of Polyether polyols network influence was studied 。In this research ternary resins and IPDI was selected as chain extension and curing agent. The different of mechanical properties of the different formula of the Polyether polyols network system. The result showed that ternary resin has obviously influence to the mechanical properties of the PET polyurethane system. In the situation of PET and ternary resin contain mass ratio, changing the quantity of IPDI until it is 1%, the polyurethane has the best mechanical properties. In the situation of the constant mole ration of IPDI, changing Polyether polyols is2%, the polyurethane has the best mechanical properties.
Keywords Polyether polyols IPDI NC mechanics performance
目 次
1 绪论 1
1.1 引言 1
1.2 NC的结构及性能研究 1
1.3 NC的国内外发展及其应用 4
1.4 本课题的主要研究内容 6
1.5 本课题的研究目的及意义 6
2 实验部分 6
2.1 实验原料及仪器 6
2.2 实验原理 7
2.3 配方及工艺条件的选择 8
2.4 实验操作 10
2.5 实验工艺讨论 10
2.6 物料的配比 11
3 结果与讨论 12
3.1 不同药品的添加对性能的影响 12
3.2 样品性能 14
结 论 18
致 谢 19
参 考 文 献 20
1 绪论
1.1 引言
硝化棉的制备方法最早见于1833 年[1]，其时法国化学家布拉克诺（Braconnot）将一系列碳水化合物，如棉花、淀粉、木材纤文等溶解在浓硝酸中，制得了一种易燃物，并命名为“木炸药”[2]，这就是硝化棉的前身。之后，人们不断对硝化棉的制造方法进行改进：雄班（Schonbein）在浓硝酸中加入浓硫酸作为吸水剂，他将所得物质取名为硝化棉，用作炸药，并取得了专利；因为当时制造这种硝化棉的工艺方法、设备很简陋，制备的硝化棉很不稳定，所以在当时没有应用到工业生产。阿贝尔Abel）在前人研究的基础上[3]，对硝化棉的安定性处理进行了改进，奠定了硝化棉工业化的基础；盖斯（Gasser）及许多俄罗斯专家用硝化棉为原料制备了无烟火药。
从人们第一次制备出硝化棉至今已有170 余年的历史。作为一种相对古老的化工产品，有人在40多年前就预言硝化棉的生命即将结束，因为当时出现了似乎可以取代硝化棉的丙烯酸树脂。然而时至今日，硝化棉不但未被取代，而且仍然在持续发展。