摘要本文采用阳离子选择性刻蚀方法合成了中空介孔二氧化硅微球。首先通过传统的Stöber法制备了尺寸大小为130 nm左右的二氧化硅微球模板。然后以二氧化硅纳米球为模板、十六烷基三甲基溴化铵为介孔模板剂和正硅酸乙酯为硅源，浓氨水、无水乙醇为反应介质，合成了的中空介孔二氧化硅微球。68588

用扫描电子显微镜、透射电子显微镜、氮气吸附-脱吸附对制得的中空介孔二氧化硅微球进行了表征。实验结果表明，所得纳米颗粒呈中空球形，分散性良好，粒径分布均一。

毕业论文关键词二氧化硅中空介孔微球 Stöber法

毕业设计说明书（论文）外文摘要

Title: Preparation of Hollow Mesoporous silica

Abstract：

This article uses the cation selective etching method synthesized hollow mesoporous silica microspheres. First of all, through the traditional Stober prepared the size is about 130 nm template silica microspheres. Then with silica nanoparticles as a template, hexadecyl trimethyl ammonium bromide as the mesoporous template agent and is ethyl silicate as silicon source, strong aqua ammonia, anhydrous ethanol as reaction medium, hollow mesoporous silica microspheres was synthesized.

By scanning electron microscope (sem), transmission electron microscopy (tem), nitrogen adsorption - adsorption of of hollow mesoporous silica microspheres have been characterized. The experimental results show that the nanoparticles are hollow spherical, good dispersion, uniform particle size distribution.

Key words silicon dioxide hollow mesoporous microspheres Stöber process

1 绪论 1

1.1 中空介孔纳米容器的制备 1

1.2 中空介孔微球 2

1.3 高纯二氧化硅的制备方法 3

1.3.1 沉淀法 3

1.3.2 溶胶－凝胶法 4

1.3.3 气相法 4

1.3.4 氟硅酸法 4

1.3.5 四氯化硅低温水解法 5

1.4 中空二氧化硅制备方法 5

1.4.1 喷雾反应法 5

1.4.2 模板法 5

1.4.3 乳液法 7

2 中空介孔二氧化硅微球的制备 8

2.1 实验药品与仪器 8

2.2 实验部分 9

2.2.1　实验原理 9

2.2.2 实验步骤 10

2.3 注意事项 11

3 中空介孔二氧化硅微球的表征测试 11

3.1 样品表征 11

3.1.1 电镜测试 11

3.2 本章小结 14

结论 15

参考文献 17

1 绪论

纳米二氧化硅[1]拥有好的分散性能、高化学纯度、表面能很大，高性能的热阻、电阻等，并且补强性、稳定性、增稠性和触变性都很好。纳米二氧化硅俗称“超微细白炭黑”，用于各行业作为添加剂、催化剂载体，石油化工，消光剂，塑料充填剂，油墨增稠剂，金属软性磨光剂，绝缘绝热填充剂，高级日用化妆品填料及喷涂材料、环保等各种领域。