摘要氧化石墨烯是一种性能优异的新型碳材料，具有较高的比表面积和丰富的表面官能团,在聚合物类复合材料具有广泛的应用前景。本文采用改进的Hummers法制备氧化石墨烯并用离子液体对其进行改性，从而制得氧化石墨烯/天然橡胶复合材料。性能测试结果表明，改性后的氧化石墨烯的加入使复合材料的正硫化时间明显上升，拉伸强度也有所提高，改善了其力学性能。此外，从导热系数以及TG的测试结果可以看出，复合材料的热学性能也有了很大的提高。同时，经过离子液体改性，氧化石墨烯在橡胶基体中的分散得到了显著改善，相比于未改性的氧化石墨烯样，改性后氧化石墨烯样各方面性能得到了进一步的提高。63624
毕业论文关键词 氧化石墨烯 离子液体 改性 复合材料 性能测试
毕业设计说明书（论文）外文摘要
Title Study on the preparation and properties of Graphene Oxide/NR composites
Abstract As a new carbon material with excellect properties,Graphene Oxide exhibits high specific surface area and surface functional groups so that it can be applicated in the polymer-based composites widely. In this paper, graphene oxide was prepared by improved Hummers method, followed by modified through ionic liquids. After that, the graphene oxide/NR composites were prepared. The results of test show that the mechanical, the vulcanization time and tensile strength of the composites were improved significantly with the addition of modified graphene oxide.In addition, test results from the thermal conductivity and TG show that thermal properties of the composites were greatly improved. Meanwhile, the dispersions of graphene oxide in the rubber matrix obtained a significant improvement compared with unmodified graphene oxide so that the performance of composites with modified graphene oxide has been improved furtherly.
Keywords: Graphene oxide， Ionic liquids， Modification， Composites， test of properties
1 绪论 1
1.1 石墨烯 1
1.1.1 石墨烯的发现与意义 1
1.1.2 石墨烯的制备 1
1.2 氧化石墨烯 2
1.2.1 氧化石墨烯的概述 2
1.2.2 氧化石墨烯的制备 3
1.2.3 氧化石墨烯的改性 4
1.2.4 离子液体的简介与应用 4
1.2.5 氧化石墨烯/聚合物复合材料的制备 5
1.3 本课题的研究目的、意义及主要研究内容 6
2 实验部分 6
2.1 主要实验仪器与实验药品 6
2.2 实验步骤 7
2.2.1 氧化石墨的制备 7
2.2.2 氧化石墨烯的制备与改性 8
2.2.3 改性氧化石墨烯/NR复合材料的制备 8
2.2.4 硫化性能测试 9
2.2.5 拉伸性能测试 9
2.2.6 撕裂性能测试 9
2.2.7 导热性能测试 9
2.2.8 TG测试 9