摘要用水热合成法制备铁掺杂ZSM-5，用XRD、NH3-TPD、EPR、BET对合成样品进行表征，并进行脱硝检测。发现PH值、体系的均匀混合程度对铁掺杂ZSM-5制备有着重要作用。EPR发现NH3的吸附氧化为绝速步.BET发现随着铁的增多比表面成对应减少。在催化脱硝中发现铁对催化脱硝有着重要作用，而且确认硅铝铁原子摩尔比为50:1:1 ZSM-5催化剂有着良好的脱硝性能和较宽的催化温度窗口。60111
毕业论文关键词 铁掺杂 ZSM-5 催化脱硝
毕业设计说明书（论文）外文摘要
Title Transition metal-doped ZSM-5 Zeolite Synthesis and Catalytic Activity
Abstract A kind of Fe-ZSM-5 was Prepared by hydrothermal synthesis , with the characterization of XRD , NH3-TPD , EPR , BET and was conducted by denitration testing. And it was found that PH value , the system's uniform mixing degree has an important role in preparing Fe-ZSM-5 . Also NH3 adsorption and oxidation step was found as the rate-determining step by EPR . And it was found that surface area was reduced with the increase of iron by BET. In addition to , in the catalytic DeNOx experiment , iron was found has an important role in catalytic denitration , and the ZSM-5 with the molar ratio of silicon alumina iron is 50:1:1 has good catalytic performance and wider temperature window .
Keywords iron ZSM-5 catalytic denitration
目录
1. 引言 1
1.1. 脱硝现状 1
1.2. ZSM-5发展情况 2
2. 实验 5
2.1. 合成 5
2.1.1. 无铁掺杂ZSM-5合成 5
2.1. 2. 铁掺杂ZSM-5合成 5
2.2. 表征 6
2.3. 催化活性测量 8
3. 结果和讨论 10
3.1. 合成部分XRD 10
3.1.1 无铁掺杂ZSM-5 XRD谱图 10
3.1.2 铁掺杂ZSM-5 XRD谱图 10
3.2 NH3-TPD检测 13
3.3. EPR检测 15
3.4 BET检测 18
3.5 脱硝分析 18
3.5.1 铁掺杂与不掺杂铁ZSM-5脱硝性能对比 18
3.5.2 不同比例铁掺杂ZSM-5脱硝性能对比 19
结 论 21
致 谢 22
参考文献 23
1. 引言
1.1. 脱硝现状
随着中国经济的发展，生活生产能耗需求大大增加，据中国国家统计局2012年1月22日公告，初步核算显示，2011年中国能源消耗总量为34.8亿吨标准煤，比2010年增长7%[1]。这意着增长了2.3亿吨标准煤，是四年来能源消费增量最多的。报告中指出中国去年（2011）煤炭消耗量比前年增长9.7%，原油增长2.7%，电力增长11.7%，天然气增长12%。这意着尽管新型能源增长很快，但煤炭依然是中国的主要能源，这在短期内很难改变。而随着燃煤剧增，由于其燃烧产生的SOx以及NOx主要空气污染物也急剧增加，这已经严重影响我国居民的身体健康。据环保部2012年夏天发布的数据显示，2011年，全国二氧化硫排放总量为2217.9万吨，工业源就占到2016.5万吨；氮氧化物排放总量为2404.3万吨，工业源则占到2404.3万吨。目前，环保部推出了大气污染防治的“最严”产业政策。环保部于2013年19日确定，将对包括19个省(区、市)的47个地级及以上城市在内的重点控制区，对火电、钢铁、石化、水泥、有色、化工等六大重污染行业及燃煤工业锅炉的新建项目，火电、钢铁、石化工业以及燃煤工业锅炉的现有项目，实施特别排放限值[2]。这使得新型脱硫脱硝技术商业化迫在眉睫。