摘要：本文通过一种简单的液相化学法制备出了棒状纳米磁性Fe3O4。该方法不需要添加任何表面活性剂。FeCl2和Na2CO3分别作为铁和碱的来源。XRD和EDS表明，制备出来的纳米Fe3O4具有高纯度、无杂质；SEM和TEM表明，纳米Fe3O4长度在400nm到1500nm之间，宽度在80nm到120nm之间。调查其他铁源和碱源对Fe3O4的纳米结构的影响，研究表明：FeCl2和Na2CO3对棒状纳米Fe3O4的形成过程是不可缺少的。VSM显示，制备出的纳米Fe3O4呈铁磁性，且饱和磁化量为74.54 emu g-1。57234

毕业论文关键词：纳米粒子，磁性材料，纳米Fe3O4，FeCl2

Abstract:Through a simple chemical liquid ,I make of a rod-like nano-magnetic Fe3O4. This method does not need to add any surfactant. FeCl2 and Na2CO3 is used as source of iron and alkali . XRD and EDS showed that nano Fe3O4 is high purity , free of impurities ; SEM and TEM shows that nano Fe3O4 is lenth between 400nm to 1500nm, and is width between 80nm to 120nm. I also investigate the impact of other sources like iron sources and alkali sources in the bases of Fe3O4 nanostructures .The study shows that FeCl2 and Na2CO3 during the formation of rod-like nano- Fe3O4 is indispensable. VSM shows that Fe3O4 nanoparticles is made with ferromagnetic , and the saturation magnetization is 74.54 emu g-1

Key word: nanoparticle, magnetic material, nano Fe3O4, FeCl2

目录

1 前言 4

1.1 纳米材料概述 4

1.2 磁性纳米材料简介 6

1.3 磁性纳米粒子的制备方法 7

1.4 纳米Fe3O4的性质 7

1.5 纳米Fe3O4的应用 8

2 实验部分 8

2.1 试剂和仪器 8

2.2 棒状Fe3O4磁性纳米材料的制备 8

2.3 材料表征 9

3 结果与讨论 10

3.1棒状纳米Fe3O4的表征与分析 10

3.2其他铁源和碱源对Fe3O4纳米结构生长形态的影响 11

3.3 磁性分析 12

结论 13

参考文献 14

致谢 15

1 前言

随着纳米科学的不断发展，人们对纳米材料的性能提出了越来越高的要求。当人们将宏观物体细分成超微颗粒(纳米级)后，它将显示出许多奇异的特性，即它的光学、热学、电学、磁学、力学以及化学方面的性质和大块固体时相比将会有显著的不同。故而，纳米材料被誉为21世纪最有发展前途的研究领域之一。同时，纳米科学技术的快速发展，给磁学这一占老的学科注入了新的生机与活力。随着纳米技术与磁学的结合，磁性材料出现了很多新的性质和现象，已成为人们研究的热点。当磁性材料的尺寸降至纳米尺度时，除了具有纳米材料常见的特点外，因为本身的磁结构，还具有一些磁性材料特有的性质。如单磁畴结构，超顺磁性，高矫顽力，磁相变温度等[1-3]。磁性纳米粒子由于特殊的超顺磁性，因而在巨磁电阻、磁性液体和磁记录、软磁、永磁、磁制冷、巨磁阻抗材料以及磁光器件、磁探测器等方而具有广阔的应用前景。目前，人们已经成功制备了各种各样的纳米材料，例如纳米金属材料，纳米半导体材料，纳米陶瓷材料，纳米有机材料，纳米磁性材料等等。其中纳米磁性材料在固定化酶、靶向药物、细胞分离、免疫分析等生物医学领域将有着重要的应用价值。