    摘要:本论文主要内容是聚合氯化铝铁絮凝剂的研制,并对制成的絮凝剂的对磷吸附性能做进一步测试。采用无水氯化铝和六水合三氯化铁按照不同的铝、铁离子摩尔比以及不同的碱化度制备聚合氯化铝铁絮凝剂,先按一定摩尔比的称取相应质量的无水氯化铝和六水合三氯化铁,在室温下按200r/min的速度搅拌15分钟后,按照欲配制的碱化度,在300r/min的搅拌速度下,添加一定量的1mol/L的氢氧化钠溶液,然后继续搅拌120分钟后制得棕红色聚合氯化铝铁溶液,定容,使得每份溶液的铝、铁离子的总浓度为0.05mol/L。48981

    结果表明,聚合氯化铝铁有良好的除浊效果,絮凝性能高于聚合氯化铝或聚合氯化铁絮凝剂。聚合氯化铝铁絮凝剂的絮凝性能与絮凝剂中的铝铁摩尔比、碱化度B、反应时间、反应温度以及滴加碱溶液的速度有关。聚合氯化铝铁絮凝剂的碱化度B可设定在0.6-2.4范围内,制备聚合氯化铝铁絮凝剂的反应时间可设定为2.5小时。

    毕业论文关键词:无机高分子絮凝剂;聚合氯化铝铁;摩尔比;碱化度。

    Study on phosphorus adsorption characteristics of polymeric aluminum ferric chloride

    Abstract: The main content of this paper is the preparation of polymeric aluminum ferric chloride ferric chloride, and further tests on the phosphorus adsorption properties of the prepared flocculant. In accordance with the different aluminum, iron ion molar ratio and different basicity of polymeric aluminum ferric chloride flocculant by anhydrous aluminum chloride and ferric chloride hexahydrate, first according to the certain molar ratio take corresponding quality of aluminum chloride, anhydrous and hydrated ferric chloride, at room temperature according to 200R / min speed stirring for 15 minutes, in accordance with the desire for preparation of alkalinity, under 300r / min of stirring speed, add a certain amount of 1 mol / L NaOH solution, and continue stirring for 120 minutes after of brownish red polymerization aluminum ferric chloride solution, constant volume, making each solution of aluminum and iron from the total concentration of 0.05mol/l. 

    The results show that the polymerization aluminum ferric chloride has good turbidity removal effect and flocculation performance is higher than that of polymerization aluminum chloride or ferric chloride flocculant polymerization. Polymeric aluminum ferric chloride flocculation and flocculation of the molar ratio of Fe and Al, alkalization degree (b), reaction time, reaction temperature and drop with alkali solution speed. Polymeric aluminum ferric chloride flocculant of basification degree (b) can be set within the range of 0.6-2.4, of preparing polymerization aluminum ferric chloride reaction time can be set to 2.5 hours.

    Key words: Inorganic polymer flocculant; polymeric aluminum ferric chloride; Molby; alkalinity.

    目录

    绪论·1

    1.1 课题研究背景·1

    1.2 絮凝剂的现状及发展趋势··2

    1.3 文献综述··3

    1.3.1 水体富营养化·3

    1.3.2 絮凝剂的定义·4

    1.3.3絮凝剂的分类··4

    1.3.4无机絮凝剂5

    1.4 聚合氯化铝铁的介绍及应用·5

    1.4.1 聚合氯化铝铁·5

    1.4.2 聚合氯化铝铁在水处理工艺领域的应用··6

    1.5本论文研究的目的和内容7

    实验部分8

    2.1 实验仪器与药品8

    2.1.1 主要原料8

    2.1.2 主要仪器设备·8

    2.2 聚合氯化铝铁絮凝剂的制备·8

    2.2.1 制备方法9

    2.2.1.1前期准备:9

    2.2.1.2 聚合氯化铝铁絮凝剂的制备,主要分为如下几个步骤9

    2.2.2不同摩尔比下的聚合氯化铝铁絮凝剂的制备··10

  1. 上一篇:年产5.8万吨电解法烧碱工段氢气处理工序的初步设计+图纸
  2. 下一篇:Flower In The Air Eau de Toilette Kenzo for women香水的仿制
  1. 数字全息术研究铁在酸性...

  2. 规整氧化铁微纳米粒子的可控制备与性能研究

  3. 可用于开环易位聚合的含硅类单体的合成研究

  4. 手性高连接配位聚合物的...

  5. 邻菲咯啉-钴(II)-二膦酸配位聚合物结构与表征

  6. 联吡啶-铜(II)-硫酸配位聚合物结构与表征

  7. 1,4-丁二酸-铅(II)配位聚合物结构与表征

  8. 杂拟谷盗体内共生菌沃尔...

  9. 中考体育项目与体育教学合理结合的研究

  10. java+mysql车辆管理系统的设计+源代码

  11. 当代大学生慈善意识研究+文献综述

  12. 电站锅炉暖风器设计任务书

  13. 河岸冲刷和泥沙淤积的监测国内外研究现状

  14. 大众媒体对公共政策制定的影响

  15. 酸性水汽提装置总汽提塔设计+CAD图纸

  16. 十二层带中心支撑钢结构...

  17. 乳业同业并购式全产业链...

  

About

751论文网手机版...

主页:http://www.751com.cn

关闭返回