摘要为了对现在建筑中广泛应用的聚氨酯材料的燃烧特性有初步的了解，运用DSC-TGA-MS-IR联用方法研究聚氨酯材料在空气氛围下的热解特性，发现热解过程主要分为释放可燃性气体的热解控制和可燃性气体燃烧放出CO2和CO的氧化还原这两个阶段，通过DSC-TG曲线的分析得到热解参数着火温度和燃尽温度并发现热解的起始对应的温度和最大热解速率所对应的温度随着温升速率的增加而向着高温区移动的特性；运用FWO法和Kissinger法两种方法对DSC曲线计算，得出了聚氨酯的热解动力学参数中的活化能和指前因子。18976
- 上一篇：聚苯胺氧化钨纳米复合物的制备研究
- 下一篇：智能水基灭火器材关键技术研究
关键词 PU 热解 动力学参数
毕业设计说明书（毕业论文）外文摘要
Title The TG and DSC analysis of PU at an air atmosphere
Abstract
In order to have a preliminary understanding for the combustion characteristics of polyurethane material which is widely used in the construction, using DSC-TGA-MS-IR studies pyrolysis characteristics of polyurethane materials in an air atmosphere, found that the pyrolysis process is pided into stages of pyrolysis control which release of flammable gas and stage of redox at which stage the gas oxidation reaction. Get ignition temperature and burnout temperature by analyzing the DSC-TG curves and found the property that with the increase of the rate of temperature rise starting corresponding temperature and maximum rate of pyrolysis temperature corresponding move toward the high temperature. Use both FWO method and Kissinger method to calculate the DSC curve, obtain
the activation energy and pre-exponential factor of PU.
Keywords PU Pyrolysis process Kinetic parameters
目 次
•1 绪论 1
•1.1研究背景 1
•1.2研究目的及意义 2
•1.3国内外研究现状 3
•1.4本课题的研究工作 3
•2 实验方法介绍 4
•2.1差式扫描量热法（Differential scanning calorimetry，简称DSC） 4
•2.2热重法（Thermo Gravimetric Analyzer） 4
•2.3质谱法 4
•2.4傅里叶红外光谱法 5
•2.5热分析联用技术 5
•2.6实验的动力学分析法 7
•3 实验结果与分析 9
•3.1实验过程 9
•3.2 实验的动力学分析 9
•3.3实验结果的图表与分析 13
结论 24
致谢 26
参考文献 27
•1 绪论
•1.1 研究背景
在经济高速发展的今天，我国也同其他国家一样，不可避免的,面临着资源严重短缺的问题。作为世界上最大的建筑市场，我国建筑中的绝大多数仍然是高能耗建筑，为了持续发展，建筑节能势在必行，而对墙体进行保温处理是建筑节能的关键，墙体保温材料也因此而备受重视。
由于PU材料不仅保温性能优越，而且力学特性和防水性能良好，所以PU材料在众多保温材料中实用价值最高，受到了广泛关注。PU材料相比于无机保温材料，其优越性较为显著，主要表现在以下几个方面：○1不易吸湿；○2导热系数小，不易传热；○3力学性能好；○4密度小，不会导致保温层过厚的问题；○5更符合环保要求。
与其他有机材料（XPS，ESP）相比，PU的优势主要表现在：○1抗裂；○2密封性；○3防水性；○4保温性；○5环保；○6抗风
表1.1 PU材料的应用和性能
分类 主要特性 用途举例