摘要：SiC 泡沫陶瓷具有耐腐蚀、耐高温、低热导率和低热膨胀系数等优异的物理性能，孔隙高度连通，是熔融金属过滤的最佳候选材料之一。本实验采用有机泡沫浸渍法来制备碳化硅多孔陶瓷， 重点介绍了碳化硅泡沫陶瓷的制备，阐述了碳化硅泡沫陶瓷的制备方法以及影响碳化硅泡沫陶瓷产品性能的因素， 该方法制得的泡沫陶瓷气孔率高、机械强度高。 毕业论文关键词： 碳化硅;多孔陶瓷;有机泡沫 21656
- 上一篇：铒掺杂硅酸铋玻璃制备及发光性能研究
- 下一篇：造孔剂法制备多孔SiC陶瓷及性能研究
Preparation of reticulated porous silicon carbide ceramics and performance study
Abstract: SiC ceramic foams are one of the most suitable candidates for the filtration of molten
metals due to their excellent properties such as high temperature resistance, corrosion resistance,
low thermal conductivity, low thermal expansion coefficient and the unique structures of
extremely interconnected cell. Organic foam impregnation w as employed to prepare porous
SiC ceramics .The preparation of silicon carbide foam ceramic are focused in this article，the
preparation methods of silicon carbide foam ceramic and factors that affect the performance of
silicon carbide foam ceramic product are introduced， The ceramic manufactured by this method
has high pore ratio and high mechanical strength.
Keywords: silicon carbide；porous ceramics；polymeric sponge
目录
1. 绪论 1
1.1. 碳化硅多孔陶瓷 . 1
1.1.1. 碳化硅介绍 . 1
1.1.2. 多孔陶瓷介绍 .. 1
1.1.3. 碳化硅多孔陶瓷的特点 1
1.1.4. 碳化硅多孔陶瓷的应用 2
1.1.5. 碳化硅多孔陶瓷添加剂 5
1.1.6. 碳化硅多孔陶瓷的制备方法 .. 6
1.1.7. 碳化硅多孔陶瓷的研究进展 .. 8
1.2. 研究目的和意义 . 9
2. 实验制备与过程 .. 10
2.1. 实验原料 10
2.2. 实验设备 10
2.3. SiC 陶瓷料浆流变性能要求 .. 11
2.4. 实验设计与工艺流程 .. 11
3. 结构控制与性能研究 . 15
3.1. 孔径大小与孔壁厚度 .. 15
3.2. 浆料粘度的影响 15
3.3. SiC 多孔陶瓷的孔隙率 16
3.4. SiC 多孔陶瓷显微结构 17
3.4.1. SiC 多孔陶瓷物相组成 .. 17
3.4.2. SiC 多孔陶瓷显微形貌 .. 18
3.5. SiC 多孔陶瓷抗压强度 20
3.5.1. 抗压强度分析与讨论 . 21
4. 结论 .. 22
致 谢 .. 23
参考文献 .. 24
1
1. 绪论
1.1. 碳化硅多孔陶瓷
1.1.1. 碳化硅介绍
碳化硅 （SiC）是用石英砂、 石油焦（或煤焦）、木屑为原料通过电阻炉高温冶炼而成。
碳化硅在大自然也存在罕见的矿物，莫桑石。 碳化硅又称碳硅石。在当代 C、N、B 等
非氧化物高技术耐火原料中，碳化硅为应用最广泛、最经济的一种。可以称为金钢砂或耐
火砂。 碳化硅是用石英砂、石油焦（或煤焦）、木屑（生产绿色碳化硅时需要加食盐）等
原料在电阻炉内经高温冶炼而成。目前我国工业生产的碳化硅分为黑色碳化硅和绿色碳化
硅两种，均为751方晶体，比重为3.20～3.25，显微硬度为2840～3320kg/mm2
。
1.1.2. 多孔陶瓷介绍
多孔陶瓷材料是以刚玉砂、碳化硅、堇青石等优质原料为主料、经过成型和特殊高温
烧结工艺制备的一种具有开孔孔径、高开口气孔率的一种多孔性陶瓷材料、具有耐高温，