菜单
  

    3.    Jawahir IS, Brinksmeier E, M’Saoubi R, Aspinwall DK, Outeiro JC, Meyer D, Umbrello D, Jayal AD (2011) Surface integrity in material removal processes: recent advances. CIRP Ann - Manuf Technol 60:603–626
    4.    Neubauer T, Poll G, Denkena B, Maiss O (2013) Fatigue life extension of rolling element bearings by residual stresses induced through surface machining. World Tribology Congress, Torino
    5.    Harris TA (2001) Rolling bearing analysis, 4th edn. Wiley, NewYork
    6.    Liu JY, Tallian TE, McCool JI (1975) Dependence of bearings fatigue life on film thickness to surface roughness ratio. ASLE Trans 18(2):144–152
    7.    Tallian TE, McCool JI (1971) An engineering model of spalling fatigue failure in rolling contact - II. The surface model. Wear 17:447–461
    8.    Guo YB, Sahni J (2004) A comparative study of hard turned and cylindrically ground white layers. Int J Mach Tools Manuf 44(2–3):135–145
    9.    Carroll RI, Beynon JH (2007) Rolling contact fatigue of white etching layer: Part I: Crack morphology. Wear 262:1253–1266
    10.    Borbe C (2001) Bauteilverhalten hartgedrehter Funktionsflaechen. Dissertation, Universitaet Hannover
    11.    Jivishov V (2008) Mikrogeometrische Einfluesse beim Weichund Hartspanen. Dissertation, Leibniz Universitaet Hannover
    12.    Knuefermann MMW, McKewon PA (2004) A model for surface roughness in ultraprecision hard turning. Ann CIRP 53(1):99–102
    13.    Toenshoff HK, Karpuschewski B, Borbe C, von Waelzlagerringen Praezisions-Hartdrehen (1997) 14th International Plansee Seminar, Reutte, Tirol
    14.    Brammertz P-H (1961) Die entstehung der oberflaechenrauheit beim feindrehen. Ind-Anz 2:25–32
    15.    Albrecht P (1959) New development in the theory of metal cutting process part 1: the ploughing process in metal cutting. Trans ASME 82(4):348–358
    16.    Denkena B, Biermann D (2014) Cutting edge geometries. CIRP Ann - Manuf Technol 63(2):631–653
    17.    Oezel T, Hsu T-K, Zeren E (2005) Effects of cutting edge eometry, workpiece hardness, feed rate and cutting speed on surface roughness and forces in finish turning of hardened AISI H13 steel. Int J Adv Manuf Technol 25:262–269
    18.    Hua J, Shivpuri R, Cheng X, Bedekar V, Matsumoto Y, Hashimoto F, Watkins TR (2005) Effects of feed rate, workpiece hardness and cutting edge on subsurface residual stress in hard turning of bearing steel using chamfer ? hone cutting edge geometry. Mater Sci Eng A 394:238–248
    19.    Hosseini SB, Ryttberg K, Kaminski J, Klement U (2012) Charaktersization of surface integrity by hard turning of bainitic and martensitic AISI 52100 steel. CIRP Procedia 1:494–499
    20.    Thiele JD, Melkote SN (2000) Effect of cutting-edge geometry and workpiece hardness on surface residual stresses in finish hard turning of AISI 52100 steel. Trans ASME 122:642–649
    21.    Thiele JD, Melkote SN (2000) Effect of tool edge geometry on workpiece subsurface deformation and through thickness residual stresses for hard turning of AISI 52100 steel. J Manuf Process 2(4):1–7
    22.    Hosseini SB, Beno T, Klement U, Kaminski J, Ryttberg K (2014) Cutting temperatures during hard turning - measurements and effects on white layer formation in AISI 52100. J Mater Process Technol 214:1293–1300
    关于切削半径在硬态切削中对滚子轴承内圈表面完整性的影响
    注:2015.3.12发表 2015.4.23 网上发表 2015.5.6德国工程生产学术会(WGP)

    分离硬态切削是用为制造高精度坚硬零件的结束过程。过去几十年,他由于更高的弹性和生产效率被认为能替代传统研磨过程。此外,硬态切削和研磨相比增加了更好的效应。过程参数像切削速度、进给量、切削轨迹影响表面区域的效果像表面粗糙度。过去几年许多研究者已经分析过这些影响。然而,他们都涉及到了一两方面表面完整性的因素。事实上由于所有研究者有不同的实验环境,这几乎是不可能去比较硬态切削对表面完整性的影响。对于总结如何去识别制造滚子轴承时伴随着增加的最佳参数数值,已经发表的研究报告都覆盖了切削速度、进给量和切削半径对主要因素(滚子轴承表面残余应力、粗糙度、微观结构和硬度)的影响。管理硬态切削测试是和分析残余应力、表面粗糙度、硬态
  1. 上一篇:刷镀机镀笔英文文献和中文翻译
  2. 下一篇:自动化级进模钣金排样英文文献和中文翻译
  1. 变频器在供水控制系统的...

  2. 柴油机连杆英文文献和中文翻译

  3. 传感元件英文文献和中文翻译

  4. FD生成的PMM数据在初步设计...

  5. 在平衡的轴向荷载下K型管...

  6. 水泥用量对暴露在高温下...

  7. 钢筋混凝土柱在火灾中的...

  8. 大众媒体对公共政策制定的影响

  9. 河岸冲刷和泥沙淤积的监测国内外研究现状

  10. java+mysql车辆管理系统的设计+源代码

  11. 电站锅炉暖风器设计任务书

  12. 酸性水汽提装置总汽提塔设计+CAD图纸

  13. 当代大学生慈善意识研究+文献综述

  14. 乳业同业并购式全产业链...

  15. 中考体育项目与体育教学合理结合的研究

  16. 杂拟谷盗体内共生菌沃尔...

  17. 十二层带中心支撑钢结构...

  

About

751论文网手机版...

主页:http://www.751com.cn

关闭返回