摘要高铌钛铝合金具有低的密度、高的熔点、比强度和高温强度以及良好的抗氧化性和抗蠕变性等优点，但是其室温塑性低是在应用化过程中的阻碍。而得到细小、均匀的显微组织是获得较好室温力学性能特别是较高室温塑性的前提条件。68266
本文从添加微量元素W来研究其对钛铝合金微观组织的作用。利用悬浮熔炼制备高铌TiAl合金铸锭，通过吸铸得到高铌TiAl合金试棒。磨制金相，采用电镜等仪器观察。结果表明，Ti-45Al-8Nb合金树枝晶大小随着W含量的增加而减少，单位体积内树枝晶的数目增加。
毕业论文关键词 高铌钛铝合金 微量元素W 微观组织
毕业设计说明书（论文）外文摘要
Title Effect of Trace Elements in Titanium Aluminum Alloy Microstructure
Abstract
High niobium titanium aluminum alloy has a low density, high melting point, strength and high temperature strength and good oxidation resistance and creep resistance and other advantages, but its low ductility at room temperature is the block in the process of the application.But getting the fine and well-distributed microstructure is the preliminary condition to obtain better mechanical properties ,especially higher ductility.This paper from the addition of trace element W to study its effect on Microstructure of titanium alloy. The prepared by levitation melting of high Nb TiAl alloy ingot, by suction casting high Nb TiAl alloy bar. Grinding metallographic, SEM observations. The results show that the dendrite size, Ti-45Al-8Nb alloy decreases with the increase of W content, the number of dendrites in unit volume increased.
Keywords High niobium titanium aluminum alloy Trace elements W
Microstructure
目 次
1 绪论 1
1.1 课题背景及研究目的和意义 1
1.2 TiAl合金的研究与应用现状 2
1.3 TiAl基合金的组织结构 3
1.4 Ti-Al-Nb 三元系合金 6
1.5 合金化元素对高铌钛铝合金的影响 7
1.6 本文研究内容 9
2 实验内容和方法 10
2.1 研究方案 10
2.2 实验材料及设备 11
2.3 实验步骤 13
2.4 分析方法 14
3 实验结果分析及讨论 14
3.1 实验结果 14
3.2 Ti-45Al-8Nb-xW(x=0,1,2)合金的凝固组织 16
3.3 显微组织的 X 射线衍射分析 19
3.4 分析及讨论 19
结 论 21
致 谢 22
参 考 文 献 23
1 绪论
1.1 课题背景及研究目的和意义
随着现代科技的发展，材料的性能极限制约着人类制造出性能更好、更高效的材料，由此看出，新型材料的开发是未来发展高新技术工业的重点研究方向。高温金属间化合物的存在让人们在高温材料领域上看到了新的曙光，不同于已经没有发展潜力的传统材料，综合力学性能处于金属和陶瓷间的金属间化合物具有诸多优点，例如普遍具有相对较低的密度、更高的强度和优良的耐热性能，正是由于具有这些特殊性能，使其在高温结构材料领域内有广阔的前景，将来可用于航空航天、汽车船舶和化学工业等领域[1]。所以，金属间化合物的研究已成为近年来材料科学中一个十分活跃的前沿领域。论文网