    摘要液相感应加热共渗处理是一项将感应加热引入到化学热处理加工中的新型表面强化技术,有着加工时间短,环境友好,节约能源、减少成本等诸多优点。本文采用液相感应加热对低碳钢在甲酰胺溶液、三乙醇胺溶液、丙三醇溶液中进行了处理,构建了加工过程中的控温装置,循环水冷装置,对所获渗层的截面硬度分布、渗层深度进行了测量;对截面的金相组织进行了观察;调整工艺参数,讨论了处理温度和保温时间对渗层性能的影响。68050

    研究结果表明:用甲酰胺试剂进行处理,其中560℃下保温10min渗层厚度可达70μm左右,最高硬度可达663.2HV0.1。用三乙醇胺溶液进行处理,试样表面的渗层明显且均匀。590℃下保温10min渗层厚度可达60μm左右,最高硬度可达680.3 HV0.1。提高保温温度和延长保温时间,均利于渗层厚度和硬度增加。丙三醇试剂用来渗碳,可明显看到试样因加热而晶粒长大。920℃处理10min渗层厚度大约100μm,最高硬度762 HV0.1。用于测量表面温度的三种热电偶连接方法,相比较效果较突出的是第二种。铜粉的添加使得热电偶温度测量端能真正接触试样的小孔底部,避免了因高温无机胶的阻隔或因小孔孔径的不合适造成热电偶测量端与试样间存在间隙而测温不准确。冷却循环水装置的添加使得靠近盛装试剂容器边缘的试剂温度升高收到抑制,从而使得溶液的蒸发量减少存在可能。

    毕业论文关键词  化学热处理,液相感应共渗,测量温度

    毕业设计说明书(论文)外文摘要

    Title  Research on the low carbon steel prepared by Liquid Induction Thermo-chemical Process                               

    Abstract

    Liquid Induction Thermo-chemical Process is a kind of brand new method which combines Induction heating and Thermo-chemical treatment to reduce soaking time, save energy and reduce production cost. Low carbon steel was treated in the formamide reagent, tri-ethanolamine reagent, glycerol reagent by Liquid Induction Thermo-chemical Process while the processing temperature was controlled and the cooling water circulating means is added. Section hardness distribution and depth of layers were measured. Metallographic organization was observed. Composition of the surface and its distribution were analyzed. The influence of processing temperature and soaking time were also analyzed. 

    The results show that, a layer as the depth is 70μm could be generated at 560℃ for 10 minutes and the maximum hardness is 663.2HV0.1 when the low carbon steel was treated in the formamide reagent. a layer as the depth is 60μm could be generated at 590℃ for 10 minutes and the maximum hardness is 680.3HV0.1 when the low carbon steel was treated in the tri-ethanolamine reagent. Propanetriol reagents were used to carburizing, a layer as the depth is 100μm could be generated at 920℃ for 10 minutes and the maximum hardness is 762HV0.1. Addition of copper powder can improve the accuracy of thermocouple. The cooling water circulating means’ added is useful.

    Keywords  Thermo-chemical treatment, Liquid Induction Thermo-chemical Process,

    Measuring Temperature

    目  录

    1 引言 1

    1.1 渗碳 1

    1.2 渗氮 2

    1.3 氮碳共渗 2

    1.4 碳氮共渗 3

    1.3.1 液体碳氮共渗 3

    1.3.2 气体碳氮共渗 4

    1.3.3 液相感应碳氮共渗

  1. 上一篇:碳纳米管热稳定性的分子动力学模拟
  2. 下一篇:镁基非晶储氢合金的取代改性以及对高氯酸铵的分解催化效应的研究
  1. 高强铝合金螺柱感应+拉弧...

  2. 钛合金表面阴极微弧液相碳氮共渗工艺的研究

  3. 钢的液相等离子电解渗入工艺研究

  4. 钨酸钆纳米材料液相合成及性质表征

  5. 复合润滑剂的液相等离子法制备

  6. 连续切片法低碳钢晶粒与...

  7. 感应热处理工艺新型连续...

  8. 电站锅炉暖风器设计任务书

  9. 酸性水汽提装置总汽提塔设计+CAD图纸

  10. 当代大学生慈善意识研究+文献综述

  11. 杂拟谷盗体内共生菌沃尔...

  12. 大众媒体对公共政策制定的影响

  13. 河岸冲刷和泥沙淤积的监测国内外研究现状

  14. 中考体育项目与体育教学合理结合的研究

  15. java+mysql车辆管理系统的设计+源代码

  16. 乳业同业并购式全产业链...

  17. 十二层带中心支撑钢结构...

  

About

751论文网手机版...

主页:http://www.751com.cn

关闭返回