摘要本课题对2mm厚的锆R60702试板的等离子焊接工艺进行了探究，通过试验找到了等离子焊接的最佳工艺参数，并对焊接后的焊缝进行了力学性能测试，显微硬度检测，显微金相观察及扫描电镜成分分析。67487
试验结果表明，当电流为100A，焊速50cm/min，离子气流量2.0L/min，可得到良好的焊缝外观成型。通过拉伸试验和显微硬度检测，焊缝区的强度较高，抗拉强度为445.13Mpa，符合标准；在焊缝区硬度值最高，约为170HV0.3，热影响区约为160 HV0.3，母材区约为150 HV0.3。金相观察发现R60702进行等离子弧焊后，焊缝区为针状马氏体组织，热影响区组织与焊缝相似，晶粒更加粗大，母材区为等轴晶组织，。扫描电镜成分分析结果表明，焊缝区及热影响区内部组织成分与母材相均为Zr，焊缝内部未受污染，焊接工艺较好。
毕业论文关键词 锆R60702 等离子弧焊 机械性能 微观组织
毕业设计说明书（论文）外文摘要
Title Study on weldability of Zirconium alloys
Abstract
This paper mainly studies weldability of 2mm thick plate of zirconium R60702 through plasma arc welding. And the optimum process parameters of plasma welding was found. mechanical properties, microhardness testing, Metallographic observation and scanning electron microscopy component analysis of the weld has been tested.
The results show that, in the welding current of 100A, the welding velocity
of 50cm/min, the plasma gas flow rate of 2.0L/min, the appearance molding is the best. Through tensile test and hardness test, the tensile strength is 445.13Mpa in weld zone, which is conform to the standard. In the weld zone, hardness value is about 170 HV0.3, which is the highest. In heat affected zone, it is about 160 HV0.3. In the parent metal zone, it is about 150 HV0.3. Metallographic observation found that the microstructure is acicular martensite in the weld zone. the grains of heat affected zone is similar to weld zone, but more coarse, the microstructure of parent metal zone is equiaxed grains. SEM analysis showed that internal components of weld zone, heat affected zone and parent metal are all Zr. It tells that the weld seam is unpolluted and the welding procedure is good.
Keywords Zirconium R60702 plasma arc welding microstructure
Mechanical properties
目 录
1 绪论 1
1.1 锆及锆合金特性及应用现状 1
1.2 锆及锆合金焊接性研究现状 2
1.3 等离子弧焊技术 4
1.4 课题的研究意义与研究内容 6
2 试验材料及设备 8
2.1 试验材料 8
2.2 试验设备 8
3 锆R60702等离子焊接工艺及焊缝成型分析 12
3.1 锆R60702等离子弧焊工艺设计 12
3.2 锆R60702等离子弧焊工艺试验 13
3.3 焊缝成型分析 15
3.4 本章小结 17
4 锆R60702焊接接头机械性能及组织成分分析 18
4.1 锆R60702焊接接头机械性能分析 18
-
上引连铸铜合金的组织和性能研究
-
AZ31镁合金板料胀形性能的研究退火实验
-
DZ4125镍基高温合金衬垫结...
-
Al-Cu合金中刃位错运动与纳...
-
相场法研究铝浓度对镍铝...
-
LabVIEW机器人双面双弧焊接过程监控系统研究
-
钛合金激光+PMIG对接焊工艺...
杂拟谷盗体内共生菌沃尔...
java+mysql车辆管理系统的设计+源代码
乳业同业并购式全产业链...
中考体育项目与体育教学合理结合的研究
大众媒体对公共政策制定的影响
河岸冲刷和泥沙淤积的监测国内外研究现状
电站锅炉暖风器设计任务书
酸性水汽提装置总汽提塔设计+CAD图纸
当代大学生慈善意识研究+文献综述
十二层带中心支撑钢结构...