摘要本文成功制备了一种加工性能很好的低温可挤注的高分子复合材料，此复合材料由共聚物树脂、耐烧蚀填料、增塑剂等添加剂共混后挤出制得。此复合材料的制备包括：一、复合材料专用树脂的制备，该专用树脂为悬浮聚合法制备的甲基丙烯酸丁酯-苯乙烯共聚物。二、甲基硅树脂、核-壳结构硅橡胶的制备，其中甲基硅树脂由甲基三甲氧基硅烷经水解缩聚法制得，核-壳硅橡胶则用乳液聚合法制备而得。三、将共聚物树脂与甲基硅树脂、核-壳结构硅橡胶及其他添加剂进行共混，对共混料进行挤出、注塑成型，并测定其力学性能、热稳定性和低温加工性能。63623
毕业论文关键词：高分子复合材料,核-壳结构硅橡胶,甲基丙烯酸丁酯,低温加工性能
毕业设计说明书（论文）外文摘要
Title Polymer composites that can be extruded and injected at low temperature
Abstract
This study prepared a kind of polymer composites. The composite material has good processing performance and can be extruded and injected at low temperature. This polymer composite material obtained by extrusion a mixture which consiste of copolymer resin, ablation resistance fillers, plasticizers and other additives. The preparation of the composite material includes: First, preparation of the special resin for the composite materials, the special resin is butyl methacrylate/styrene copolymer obtained by suspension polymerization method. Second, the preparation of methyl silicone resin and silicone rubber of core-shell structure. Methyl silicone resin prepared by Methyl trimethyl silane via hydrolytic condensation while emulsion polymerization method was used to prepare silicone rubber of core-shell structure. Third, the copolymer was blended with silicone rubber of core-shell structure, methyl silicone resin and other additives, then extruded and injected the mixture. Test its mechanical properties, thermal stability and processing performance at low temperature.
Keywords Polymer composites, silicone rubber of core-shell structure, BMA, processing performance at low temperature
1 绪论 1
1.1 复合材料概述 1
1.1.1 复合材料的概念 1
1.1.2 复合材料的分类 1
1.2 高分子复合材料的概述 1
1.2.1 高分子复合材料的概念 1
1.2.2 高分子复合材料的分类 2
1.3 高分子复合材料在火药包覆材料中的应用 4
1.3.1 对包覆材料的要求 4
1.3.2 常用包覆材料的种类及其优缺点 5
1.4 本文的研究内容及意义 6
2 核-壳结构硅橡胶粒子的制备与表征 7
2.1 前言 7
2.2 实验部分 7
2.2.1 实验原料及仪器 7
2.2.2 有机硅共聚物（PSi）种子乳液的制备 8
2.2.3 核-壳结构硅橡胶粒子的制备 8
2.2.4 测试表征方法 9
2.3 结果与讨论 10
2.3.1 核-壳结构硅橡胶粒子的红外光谱分析 10