摘要本文主要研究了溴化丁基橡胶的补强体系和硫化体系，对溴化丁基橡胶配方进行优化设计。采用单因素法分别对硫磺含量与炭黑含量对溴化丁基橡胶硫化胶的性能来进行了研究。结果表明，硫磺含量与炭黑含量对溴化丁基橡胶的力学性能都有很大的影响。在其他填料不变时，随着炭黑用量的增大，溴化丁基橡胶的拉伸强度、撕裂强度、硬度增大；断裂伸长率减小。在其他填料不变时，溴化丁基橡胶的力学性能在硫含量为0.3phr时达到最优值。综合实验结果可得,当炭黑用量为55phr、硫磺用量为0.3phr时，硫化胶的性能最优。关键词 炭黑 硫磺 溴化丁基橡胶 力学性能8304
- 上一篇：水处理剂羟基乙叉二膦酸（HEDP）的制备
- 下一篇：半导体纳米材料的制备及应用
毕业设计说明书（论文）外文摘要
Title The cooperation system of BIIR
Abstract
This paper studied the modification of BIIR. By changing the content of sulfur and carbon black, BIIR achieve good mechanical properties. The results showed that the amount of sulfur and carbon black had a great impact on the mechanical properties of BIIR. The more carbon black content the better mechanical properties of the BIIR. When the content of sulfur was 0.3 phr, the mechanical properties of BIIR were best. Comprehensive analysis of experimental results, when the amount of carbon black was 55 phr and the amount of sulfur was 0.3 phr, BIIR of the best mechanical properties.
Keywords carbon black sulfur BIIR mechanical properties
目录
1 绪论 1
1.1 溴化丁基橡胶的简介 1
1.2 溴化丁基橡胶的结构与特性 1
1.3 溴化丁基橡胶的配合体系 1
1.3.1 溴化丁基橡胶的补强体系 2
1.3.2 溴化丁基橡胶的硫化体系 3
1.3.3 溴化丁基橡胶的增塑体系 4
1.3.4 溴化丁基橡胶的其他配合体系 5
1.4 溴化丁基橡胶的应用研究 5
1.4.1 轮胎胎面 5
1.4.2 医药用密封橡胶 6
1.4.3 设备防腐衬里 6
1.4.4 化学电容器与空调器胶管的密封 6
1.4.5 其他 6
1.5 本论文的主要研究内容 7
2 溴化丁基橡胶补强体系的研究 7
2.1 引言 7
2.2 实验部分 7
2.2.1 实验药品 7
2.2.2 实验仪器 7
2.2.3 试样制备 8
2.2.4 性能测试 8
2.3 结果与讨论 9
2.3.1 硫化特性 9
2.3.2 拉伸性能 10
2.3.2 撕裂性能 13
2.3.3 邵A硬度 13
2.4 本章小结 14
3 溴化丁基橡胶硫化体系的研究 15
3.2.1 实验药品 15
3.2.2 实验仪器 15
3.2.3 试样制备 15
3.2.4 性能测试 16
3.3 结果与讨论 17
3.3.1 硫化特性 17
3.3.2 拉伸性能 17
3.3.3 撕裂性能 20
3.3.4 邵A硬度 20
3.4 本章小结 21
结论 22
致谢 23
参 考 文 献 24
1 绪论
1.1 溴化丁基橡胶的简介