摘要本论文采用液相沉淀法制备草酸钴，通过改变反应条件，包括沉淀剂种类、沉淀剂浓度、钴盐种类和分散剂种类分别获得结晶性不同的产物，用X-射线衍射(XRD)、扫描电子显微镜(SEM)、拉曼光谱(Raman)等手段对产物的结构和形貌进行表征；通过热分析手段（TG和DTA）考察产物对高氯酸铵热分解反应过程的影响，评价其催化性能。实验结果表明，改变制备反应条件会影响产物草酸钴的粒径和形貌，但草酸钴热分解性能差别较小，最终对AP热分解的催化作用差别较小。63936
毕业论文关键词 草酸钴 液相沉淀法 催化活性 高氯酸铵
毕业设计说明书（论文）外文摘要
Title Preparation and Catalytic Properties of CoC2O4·2H2O
Abstract Cobalt oxalate powders were prepared by precipitation under different conditions. The as-prepared samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Some samples were mixed with AP to study their catalytic properties. The results showed that samples with different morphology can be obtained under different conditions. However, these samples had little differences in catalytic activity.
Keywords Cobalt oxalate, Precipitation, Catalytic activity, Ammonium perchlorate
1绪论 1
1.1 草酸钴的制备方法 1
1.2 高氯酸铵的热分解 3
1.3 草酸钴制备的研究进展 5
1.4 本论文的主要内容 6
2 草酸钴的制备与表征 7
2.1 试剂与仪器 7
2.2 草酸钴的制备 7
2.3 草酸钴的表征 8
2.4 结果讨论与分析 8
2.5 本章小结 12
3 草酸钴的热分解性质研究 13
3.1 草酸钴热分解实验 13
3.2 结果分析与讨论 13
3.3 本章小结 14
4 草酸钴的催化性能研究 15
4.1 草酸钴催化高氯酸铵热分解实验 15
4.2 结果讨论与分析 15
4.3催化机理讨论 17
4.4 本章小结 17
结论 18
致谢 19
参考文献 20
1 绪论
作为一种重要的催化材料，草酸钴由于具有稳定的晶体结构，特殊而多样的晶体形貌，较强的活性，较大的比表面积，使其在催化方面具有重大的用途。同时，由于钴作为过渡金属，特殊的微观结构和其价态的多样性，导致钴的化合物在催化方面具有重要作用[1]，而通过草酸钴可以制得钴粉[2]，氧化钴[3,4]等，均是作为催化剂的良好材料。因此，制备出具有良好形貌与催化性能的草酸钴，具有较大意义。
高氯酸铵（AP）是复合改性双基推进剂和复合推进剂中最常用的氧化剂[5]，含量占60%～80%，其热分解特性对推进剂的燃烧过程起到重要的作用，被大量应用在火箭助推剂方面。但由于高氯酸铵的分解温度较高，分解速率不大，所以一般应用时必须加入催化剂来催化其分解，达到助推的作用。常用的催化剂包括过渡金属草酸盐[6]，钙钛矿复合氧化物[7]，过渡金属氧化物[8]和过渡金属微粒[9]等，一般所用催化剂的粒径为纳米或者微米级[10]。而草酸钴对于高氯酸铵的分解有着较强的催化作用[11]，能使AP在较低温度下以较大速率进行分解，短时间内产生大量的热，满足推进剂的需要，是复合固体推进剂中高氯酸铵分解的良好催化剂。