摘要：二氧化锰纳米材料由于其优异的电化学、催化、吸附性能已被大量地研究并广泛应用于锂离子电池、超级电容器、催化等方面。目前文献中已报道的合成二氧化锰纳米材料的方法主要有二价锰离子氧化法、高锰酸钾还原法、二氧化锰前驱体水热转化三种方法。本文即采用以高锰酸钾为锰源，以橙子皮汁为还原剂，采用水热法绿色化合成前驱体，再通过高温煅烧得到二氧化锰梭状纳米材料。通过SEM，XRD，TG-DTA等方法对反应物进行了表征。62458
毕业论文关键词：二氧化锰，水热法，橙子皮汁
Abstract: Manganese dioxide nano-materials, has been extensively studied and widely used in lithium ion batteries, super capacitors, catalysis, etc. due to its excellent properties of electrochemical, catalytic, adsorption. Reported literature of the synthesis of manganese dioxide nano-materials are mainly focused on three methods of manganese-ion oxidation, reduction process of potassium permanganate and hydrothermal transformation reaction of manganese dioxide precursor. In this paper, potassium permanganate was used as the source of manganese, orange peel-extracting solution was used as reductant, and in the way of green synthesis of complex precursor by hydrothermal method, and manganese dioxide spindle nano- material is obtained by high temperature calcination. The products have been characterized by SEM, XRD, TG - DTA methods.
Keywords: hydrothermal method, manganese dioxide, orange peel-extracting solution
1 引言 4
1.1 纳米材料简介及特性 4
1.2 纳米合成方法简介 4
1.3 锰基氧化物纳米材料的性能，合成方法，应用进展 5
1.4 本论文的选题思路及主要研究内容 7
2 实验部分 8
2.1 仪器与试剂 8
2.1.1 仪器 8
2.1.2 试剂 8
2.2 实验步骤 8
2.2.1 材料合成 8
2.2.2 材料表征 8
3 实验结果与讨论 8
3.1 产物分析 8
3.1.1 煅烧前的前躯体 8
3.1.2 煅烧后的金属氧化物 10
3.2 产物形貌分析 12
3.2.1 前驱物形貌分析 12
3.2.2 煅烧所得锰氧化物的成分分析 16
结 论 18
参考文献 19
致 谢 22
1 引言
1.1 纳米材料简介及特性
纳米科学技术是在从20世纪80年代末、90年代初开始，逐步发展起来的具有前沿性、交叉性的新兴学科。它是指在1~100nm之间的纳米尺度上研究物质的特性以及相互作用，并且以及利用这些特性的多学科交叉的科学和技术。纳米材料是指结构单元尺寸小于100 nm的晶体或非晶体，是处于原子簇和宏观物体交界的过渡区域[1-2]。
纳米材料特有的结构使其具有一般宏观物质所不具有的物理特性，这些特性包括表面效应、小尺寸效应、量子尺寸效应和宏观量子隧道效应。