摘要：以甲基丙烯酸为原料制备多孔聚丙烯酸水凝胶作为吸附剂，研究了其对水中罗丹明B的吸附行为。考察了pH值、吸附时间、罗丹明B初始浓度、多孔聚丙烯酸水凝胶的用量对吸附性能的影响。结果表明，在室温下，pH为2.0左右，罗丹明B初始浓度为2.0mg/L，水凝胶用量为0.0025g/mL且吸附9h达到最佳吸附效果，吸附率可达到85.3%。同时考察了多孔聚丙烯酸水凝胶吸附罗丹明B后的释放及其重复利用性。27842
- 上一篇：N-[5-（4-溴苯基）-1,3,4-噻二唑-2-基]-N'-3-硝基苯甲酰基脲的合成与结构表征
- 下一篇：8-羟基喹啉及其衍生物金属锌配合物新型发光离子液体的合成及性能研究
毕业论文关键词：聚丙烯酸；水凝胶；吸附；罗丹明B
Study on The Adsorption Properties of Porous Polyacrylate Hydrogel of Rhodamine B
Abstract：Preparation of porous polyacrylate hydrogel as adsorbent by using methyl methacrylate as raw material，the adsorption behavior of water on the Rhodamine B．The effects of pH value，adsorption time，initial concentration of Rhodamine B，porous polyacrylic acid hydrogel dosage on the adsorption properties． The results showed that at room temperature，pH is about 2.0，when the initial concentration of Rhodamine B was 2.0mg/L，hydrogel dosage for 0.0250g/10.0mL，adsorption 9h adsorption effect is the best，the adsorption rate reached85.3%．The porous polyacrylate hydrogel adsorption Rhodamine B after release and reuse．
Key Words：Acrylic acid;Hydrogel;Adsorption;Rhodamine B
目 录
摘 要 1
引 言 1
1 实验部分 2
1.1 仪器与试剂 2
1.2 多孔聚丙烯酸水凝胶的制备 2
1.3 吸附率的测定 3
1.4 吸附实验 3
1.4.1 pH值对吸附的影响 3
1.4.2 吸附时间对吸附的影响 3
1.4.3 罗丹明B初始浓度对吸附的影响 3
1.4.4 水凝胶的用量对吸附的影响 4
1.5 多孔聚丙烯酸水凝胶吸附罗丹明B后的释放及重复利用性 4
2 结果与讨论 4
2.1 多孔聚丙烯酸水凝胶对水中罗丹明B吸附的影响因素 4
2.1.1 pH值对吸附的影响 4
2.1.2 吸附时间对吸附的影响 5
2.1.3 罗丹明B的初始浓度对吸附的影响 6
2.1.4 水凝胶的用量对吸附的影响 6
2.2 水凝胶吸附罗丹明B后的释放及重复利用性 6
2.3 水凝胶红外光谱分析 7
3 结 论 8
参考文献 8
致 谢 11
多孔聚丙烯酸水凝胶对水中罗丹明B的吸附性能研究
引 言
近年来由于工业化的快速进展，有机染料已成为当前重要的水体污染源之一。染料废水因其组成成分复杂、颜色深、毒性强、浓度高、排放量大、分布面广和难降解的特性，从而成为难处理的工业废水[1]。罗丹明B是一种人工合成的有机染料，曾经用作食品添加剂，但研究发现其对人体具有严重致癌性和致突变性，且溶于水难降解。处理有机污染物常用化学氧化法[4-6]，生物氧化法[7-9]和物理吸附法[10-13]。国内外已采用多种方法对如何使废水脱色进行了研究，主要有吸附法、光催化降解、电解法、臭氧化法、离子交换法、生物法等[1,2]。其中，吸附法由于不引入新的污染物而且可以富集分离有机污染物，实现废物资源化，因而受到广泛研究[3]。常用的吸附剂主要为各种类型的多孔性高比表面积材料，如活性炭、高岭土、天然大分子及其复合材料等[14]。但它们存在吸附效果不好、适用pH值范围小、成本太高等问题[1-3]。所以寻找性能优良的新型的吸附剂一直是当前处理染料废水急需解决的一大难题。